3M Scotch-Weld DP8010 Blue Cartridge 10:01 Mix Ratio, Low Surface Energy Bonder (Polypropylenes, Polyethylenes, TPO, etc) Acrylics Adhesive

Description

3M Scotch-Weld Structural Plastic Adhesive DP8010 Blue is a two-part acrylic adhesive specially formulated to bond many low surface energy plastics, including many grades of polypropylene, polyethylene, and thermoplastic elastomers (TPEs) without special surface preparation.

When using a Duo-Pak (DP) size adhesive, rely on 3M dispensing equipment for convenient and accurate metering, mixing and dispensing. Creates a Strong Bond on Low Surface Energy Plastics Structural bonds can be achieved without special surface treatments such as chemical etching, plasma, flame, or corona treatment or priming. Simply wipe the surfaces with isopropanol to remove mold release agents, dust dirt, etc. 3M Scotch-Weld Structural Plastic Adhesive DP8010 Blue also bonds metals, ceramics, and wood and most other plastics. It is slightly flexible when cured. We also formulate this adhesive with 8 mil spacer beads for bond line spacing. Recommended Applications Joining plastics to metals, such as in the manufacture or repair of appliances Bonding low surface energy plastics without priming Impact resistance composite bonding Manufacture or repair of various sporting goods equipment Low surface energy plastics such as polypropylene, polyethylene and thermoplastic elastomers (TPEs) Our 3M Scotch-Weld Acrylic Adhesive DP8010 starts with medium viscosity for controlled dispensing and spreads to sufficiently wet out the surface. The mix ratio is 10:1 and provides a 10 minute work life. The adhesive reaches handling strength in approximately 1 hour and is fully cured in 8-24 hours (at 72 F /22 C). Easy Adhesion with Acrylic Acrylic adhesives are two-part adhesives that provide excellent bond strength and durability. Often referred to as epoxy adhesives or epoxy glue, acrylics actually belong to a separate chemical family with their own unique characteristics. This very unique adhesive bonds LSE plastics without priming or other surface treatments.

Product Features

• Creates strong bond on low surface energy plastics (LSE) such as polyolefin with minimal or no surface prep require
• 10 minute work life with 60 minute handling strength
• Formulated to bond multi-material assemblies such as LSE plastics, thermoplastics, composites and metals

• Ability to Bond Dissimilar Substrates
  Ability to Structurally Bond Polyolefins
  Room Temperature Cure
  Excellent Water and Humidity Resistance
  Very Good Chemical Resistance
  One Step Process – No Pre-Treatment of the Substrates Needed
  Solvent-free Adhesive System
  Convenient Hand-Held Applicator System
  Contains 0.008 glass beads for bondline thickness control
  Available in Bulk

Typical Uncured Physical Properties

Attribute Name : Temperature Value
Base Color : Blue
Accelerator: Color White
Base Resin: Methacrylate
Accelerator Resin: Amine
Base Net Weight : 8 8.4 lb/gal
Accelerator Net Weight: 8.7 9.15 lb/gal
Base Viscosity : 22 C (72 F) 15000 30000 cP
Accelerator Viscosity: 22 C (72 F) 35000 55000 cP