Permabond TA4610 Polyolefin (PE, PP), Teflon (PTFE) & Rubber Bonder Thick Gel 12-15 min Acrylic MMA Adhesive Off-White

Description

Permabond TA4610 is a 2-part, 1:1 toughened acrylic adhesive. It has been developed to bond low surface energy plastics such as polypropylene, polyethylene, Teflons, and rubbers – with no primer or expensive surface treatment required. It can also be used to bond a wide variety of other materials such as metals and composite materials and ideal for bonding dissimilar surfaces.

Popular for bonding:

PE, HDPE, LDPE, UHMW, PP, PPCO, PPHO, COPP, HOPP, Natural Rubbers, Synthetic Rubbers, Teflon, PTFE

TA4610 is a part of a 4-formula Family:

Grade	Handling Strength	Set Time / Pot Life	Notes
TA4605	~25 minutes	5-10 minutes	Fast set, gel consistency, off-white, fast set
TA4610	~50 minutes	12-15 minutes	Longer pot life, gel consistency, off-white
TA4611	~35 minutes	10-15 minutes	Medium Pot Life, Thin Flowable, Low odor, clear
TA4631	~40 minutes	12-18 minutes	Longer Pot Life, Thin Flowable, Low odor, clear

TA4610 is also a substitute / backup formula for these formulas:

• 3M DP8005
• 3M DP8010
• Scigrip SG400 LSE

Features and Benefits:

• Adhesion to a wide variety of substrates
• Thick Gel Formula, Thixotropic, Non-Sagging, Gap-Filling
• Full cure at room temperature
• Set time is 12-15 min
• Bonds to polyolefins
• No primer required
• No need to flame-treat or plasma treat-surfaces beforebonding
• Excellentimpact & sheer strength
• Excellentchemical resistance

Ideal Surfaces / Works With:

• Most Metals (Mild Steel, Stainless Steel, Aluminum, etc)
• Most Plastics & In particular the hard-to-bond Low-Energy Plastics
• Composites
• Carbon Fiber
• FRP (fiber reinforced plastics)
• GRP (glass reinforced plastics)
• ABS,
• Polycarbonate
• PVC
• PA6
• PET-G
• PE-P
• EPDM & Rubbers
• E- Coatings
• Polypropylenes (PPCO, PPHO, and related)
• Polyethlyenes (LLDPE, LDPE, MDPE, HDPE, UHMW, etc)
• PTFE / Nylon

Physical Properties of Uncured Adhesive

	TA4610 A	TA4610 B
Chemical Composition	Methacrylate	Methacrylate
Color	Off-white	Almost colorless
Mixed Color	Off-white
Viscosity @ 25C	200,000-500,000 mPa.s (cP) Thixo paste	20,000-30,000 mPa.s (cP)
Specific gravity	1.0	1.0

Typical Curing Properties

Ratio to Use	1 : 1
Maximum gap fill (NB: Contains microparticles to control gap)	1 mm (0.04 in)
Pot life (2g+2g) @23C	5-8 minutes
Fixture time (0.1 N/mm shear strength is achieved) @23C	12-15 minutes
Handling time (0.3 N/mm shear strength is achieved) @23C	40-50 minutes
Working strength @23C	6-8 hours
Full cure @23C	36-48 hours

Comparable to 3M DP8005, DP 8010, and DP-8010

ApplicationInstructions

1. Surface Prep: Ensure surfaces are clean, dry, and grease-free. Use Isopropyl (rubbing alcohol) wipe if necessary.

2. Mixing & Dispensing: Use a static mixer to apply a thin, even bead of mixed adhesive.

3. Assembly & Clamping: Press parts firmly and maintain pressure until handling strength is achieved.

4. Curing Notes: Adhesive cures best inside joints (anaerobic). Adhesive exposed to air may remain tacky for an extended time (not a defect, just a characteristic, it will eventually lose it’s tackness). Remove excess before curing.

Avoiding Common Issues

Leaving large beads sticky residue.

One side exposed to air tacky, sticky surface. or crystalization or crystal-like curing

Not clamping long enough weak bond.

Stressing before full cure joint failure.

Always allow full cure before loading.

Troubleshooting

Still tacky? Exposed to air, not a bond failure, allow it to keep curing, can take a while to lose tackiness.

Crystalization? Exposed to air, not a bond failure, allow it to keep curing, can take a while to lose tackiness.

Slow to grab?Possibly TA4610 (longer cure) or surface contamination.

Joint failed? Likely due to early stress or insufficient clamping.

Note:This product willNOTset in temperatures below 50F (10C) Make sure to keep the material warm throughout the curing process.